Zytel PA66 70G43L the NC010 DuPont nylon resin 43% glass fiber DuPont Performance Polymers Product Description:? 43% glass fiber reinforced polyamide 66 PA66 DuPont distributor of professional-quality professional services agent original package fake a compensable Ten filler / reinforcing material glass fiber reinforced materials, Unit Test Method 43% by weight of filler release characteristics lubricating additive lubricant physical properties of dry density after adjustment 1.49 - g / cm3 ISO 1183 ISO 294-4 shrinkage vertical flow direction 1.0 - 0.30% flow direction -% Water absorption 24 hr 0.90 -% ASTM D570 73 ° F, 24 hr, 0.0787 in 4.7 -% ISO 62 balance, 73 ° F, 0.0787 in, 50% RH 1.5 - % ISO 62 viscosity 130-- Unit Test Method Unit Test Method cm3 / g ISO 307 Hardness Dry Conditioned Rockwell Hardness ISO 2039-2 M-Scale 105 90 R-Scale 125 118 Mechanical Dry Conditioned pull stretch modulus 2.03E + 6 1.60E + 6 psi ISO 527-2 tensile stress (fracture) 32600 23200 psi ISO 527-2 tensile strain (fracture) 3.0 4.0% ISO 527-2 tensile creep modulus ISO 899 Unit Test 1.15E + 6 psi flexural modulus 1.74E + 6 1.29E + 6 psi ISO 178 bending stress 49300 37700 psi ISO 178 Impact Dry Conditioned - -1 1 hr - 1.57E + 6 psi 1000 hr Method Charpy notched impact strength ISO 179 / 1eA -40 ° F 5.2 5.2 ft · lb / in2 -22 ° F 5.7 5.7 ft · lb / in2 73 ° F 7.6 9.0 ft · lb / in2 simply supported beam without notched impact strength ISO 179 / 1eU -22 ° F 40 36 ft · lb / in2 73 ° F 48 50 ft · lb / in2 Notched Izod Impact Strength ISO 180 / 1A -40 ° F 5.2 5.2 ft · lb / in2 -22 ° F 5.7 5.2 ft · lb / in2 73 ° F 6.7 7.6 ft · lb / in2 unnotched Izod impact strength ISO 180 / 1U -22 ° F 50 31 ft · lb / in2 73 ° F 50 43 ft · lb / in2 Thermal Performance Unit Test Method Heat Deflection Temperature dry adjusted 66 psi, without annealing 504 - ° F ISO 75-2 / B 264 psi, without annealing 491 - ° F ISO 75-2 / A glass transition temperature 3176-- ° F ISO 11357-2 Vicat softening temperature of 491 - ° F ISO 306 / B50 melting temperature of 3 504 - ° F ISO 11357-3 linear thermal expansion coefficient of ISO 11359-2 flow 8.3E-6 - in / in / ° Unit Test Method Surface Resistivity in / in / ° F dry electrical performance after adjustment - - F Transverse 4.4E-5 1.0E + 12 ohm IEC 60093 volume resistivity> 1.0E + 15 1.0E + 12 ohm · cm IEC 60093 Dielectric Strength 690 - V / mil IEC 60243-1 relative permittivity IEC 60250 100 Hz 4.50 - 1 MHz 4.10 4.90 dissipation factor IEC 60250 100 Hz 0.010 - 1 MHz 0.015 0.060 after adjustment flammable dry Unit Test Method burn rate (0.0394 in) 1.1 - in / min ISO 3795 flammability rating IEC 60695-11-10, -20 0.0280 in HB - 0.0591 in HB - LOI 23 -% ISO 4589- Units mold filling analysis Melt density Dry Conditioned 1.29 - g / cm3 Specific Heat Capacity of Melt 0.490 - Btu / lb / ° F Thermal Conductivity of Melt 1.7 - Btu · in / hr / ft2 / ° F